WSS-M1A367-A11/A50
STEEL, SHEET, HOT ROLLED, HIGH STRENGTH,SOLID SOLUTION STRENGTHENED,BAKE HARDENABLE
The materials defined by these Global specifications are fully killed, fine grained, The materials defined by these Global specifications are fully killed, fine grained, high strength steel sheet with specified minimum yield strength between 180 MPa and 550 MPa and good forming, joining, and painting characteristics.high strength steel sheet with specified minimum yield strength between 180 MPa and 550 MPa and good forming, joining, and painting characteristics.
Material:
CR180/210/240/270, CR180/210/240/270/300B2,CR240/270/300/340/380/420/500LA, HR270/300/340/380/420/500/550LA
Width: Customer's Requirement
Application: released originally for automotive body and chassis parts.
Thickness: 0.5~6.0mm
Type: Coil, Sheet, Plate
Tolerance: Min Width Tolerance ±0.1
Variant
|
A11
|
A12
|
A13*
|
A14*
|
Common Global Grade Name
|
CR180
|
CR210
|
CR240
|
CR270
|
Yield Strength
MPa (min) |
180 | 210 |
[240]
|
[270]
|
Yield Strength
MPa (max) |
240 | 270 |
[300]
|
[330]
|
Tensile Strength
MPa (min) |
300 | 320 |
[340]
|
[360]
|
ASTM Total
Elongation, % (min) |
35 | 33 |
[30]
|
[28]
|
EN Total
Elongation, % (min) |
33 | 31 |
[28]
|
[26]
|
JIS Total
Elongation, % (min) |
39 | 37 |
[34]
|
[32]
|
ravg (min)
|
1.3 | 1.3 | [1.1] | [1.0] |
n value (min) | 0.2 | 0.19 | [0.15] | [0.14] |
* Variants shown with an asterisk and gray typeface are not in the Global material strategy and should not be used without approval from the Sheet Metal Tech Club. Sources for these grades may not exist in your region. Contact Product Development Materials Engineering for assistance or gmfs@ford.com for help in locating the responsible engineer.
Variant
|
A21
|
A22
|
A23
|
A24*
|
A25*
|
Common Global Grade Name
|
CR180B2
|
CR210B2
|
CR240B2
|
CR270B2
|
CR300B2
|
Yield Strength
MPa (min) |
180
|
210 | 240 | 270 | 300 |
Yield Strength
MPa (max) |
240 | 270 | 300 | 330 | 360 |
Tensile Strength
MPa (min) |
300 | 320 | 340 | 360 | 390 |
BHI, MPa (min)
|
30 | 30 | 30 | 30 | 30 |
ASTM Total
Elongation, % (min) |
35 | 33 | 30 | 28 | 26 |
EN Total
Elongation, % (min) |
33 | 31 | 28 | 26 | 24 |
JIS Total
Elongation, % (min) |
39 | 37 | 34 | 32 | 30 |
ravg (min)
|
1.3
|
1.1
|
1.1
|
0.9
|
0.9
|
n value (min)
|
0.19 | 0.17 | 0.17 |
0.15
|
0.14
|
Variant
|
A33
|
A34
|
A35
|
A36
|
A37
|
A38
|
A39*
|
Common Global Grade Name
|
CR240LA
|
CR270LA
|
CR300LA
|
CR340LA
|
CR380LA
|
CR420LA
|
CR500LA
|
Yield Strength
MPa (min) |
240 | 270 | 300 | 340 | 380 | 420 | 500 |
Yield Strength
MPa (max) |
320 | 350 | 380 | 420 | 460 | 520 | 600 |
Tensile Strength
MPa (min) |
320 | 330 | 370 | 410 | 450 | 480 | 560 |
ASTM Total
Elongation, % (min) |
28 | 26 | 24 | 22 | 20 | 18 | 16 |
EN Total
Elongation, % (min) |
26 | 24 | 22 | 20 | 18 | 16 | 14 |
JIS Total
Elongation, % (min) |
32 | 30 | 28 | 26 | 24 | 22 | 20 |
n value (min)
|
0.15 | 0.15 | 0.14 | 0.13 | 0.12 | 0.11 | 0.09 |
* Variants shown with an asterisk and gray typeface are not in the Global material strategy and should not be used without approval from the Sheet Metal Tech Club. Sources for these grades may not exist in your region. Contact Product Development Materials Engineering for assistance or gmfs@ford.com for help in locating the responsible engineer.
|
A44
|
A45
|
A46
|
A47
|
A48
|
A49
|
A50
|
Common Global Grade Name
|
HR270LA
|
HR300LA
|
HR340LA
|
HR380LA
|
HR420LA
|
HR500LA
|
HR550LA
|
Yield Strength
MPa (min) |
270 | 300 | 340 | 380 | 420 | 500 | 550 |
Yield Strength
MPa (max) |
350 | 380 | 420 | 460 | 520 | 600 | 650 |
Tensile Strength
MPa (min) |
330 | 370 | 410 | 450 | 480 | 560 | 610 |
ASTM Total
Elongation, % (min) |
29 | 27 | 25 | 23 | 22 | 20 | 18 |
EN Total
Elongation, % (min) |
27 | 25 | 23 | 21 | 20 | 18 | 16 |
JIS Total
Elongation, % (min) |
33 | 31 | 29 | 27 | 26 | 24 | 22 |
n value (min)
|
0.15 | 0.14 | 0.13 | 0.12 | 0.11 | 0.09 | 0.08 |