Carbon steel and spring steel are important materials that have received much attention. Their unique performance characteristics and wide range of applications make them an integral part of the industry. Give us an in-depth understanding of the performance characteristics of carbon steel and spring steel and their applications in different fields.
Carbon steel performance characteristics and uses
1. Strength and durability:
Carbon steel is known for its excellent strength and durability. It can withstand high pressures and loads and is suitable for construction, machine building and tool making.
2. Plasticity and machinability:
Although carbon steel has excellent hardness and strength, it still has good plasticity and machinability. This characteristic allows it to be molded into various forms to meet the needs of different fields.
3. Corrosion resistance:
Although not as resistant to corrosion as stainless steel, under the right conditions, carbon steel still has relative corrosion resistance. It is suitable for the manufacture of some structures and components under the requirement of low cost.
4. Cost effectiveness:
Compared with other alloy steels, carbon steel has a lower cost and is easy to obtain. This makes it widely used in large-scale manufacturing.
In terms of application, carbon steel is widely used in the construction industry, mechanical engineering, automobile manufacturing, furniture manufacturing and other fields.
Performance characteristics and uses of spring steel
1. High elasticity and toughness:
Spring steel has excellent elasticity and toughness, and can recover after being stressed. This makes it ideal for all types of spring manufacturing.
2. Wear resistance:
Spring steel has high wear resistance and is suitable for applications requiring high frequency use and friction.
3. Fatigue resistance:
Spring steel has good fatigue resistance and can maintain stable mechanical properties for a long time.
4. Processability:
It has good machinability and is suitable for manufacturing various types of springs.
Spring steel is mainly used in automobile manufacturing, mechanical engineering, electronic equipment, industrial products and other fields of spring manufacturing.
| Stahl bezei chnu ng | Stahl bezei chnu ng | weich geglü ht (+A) oder weich geglü ht und leicht nach gewal zt (+LC) | weich geglü ht (+A) oder weich geglü ht und leicht nach gewal zt (+LC) | weich geglü ht (+A) oder weich geglü ht und leicht nach gewal zt (+LC) | weich geglü ht (+A) oder weich geglü ht und leicht nach gewal zt (+LC) | kaltg ewalz t c (+CR) | kaltg ewalz t c (+CR) | vergü tet d (+ QT) | vergü tet d (+ QT) |
| Kurz name | Werk stoff- num ber | Rp0,2 e N/m m2 max. | Rm e N/m m2 max. | A80 e % min. | HVe max. | Rm e N/m m2 max. | HVe max. | Rm e N/mm2 | HVC |
| C55S | 1.1204 | 480 | 600 | 17 | 185 | 1070 | 300 | 1100 bis 1700 | 340 bis 520 |
| C60S | 1.1211 | 495 | 620 | 17 | 195 | 1100 | 305 | 1150 bis 1750 | 345 bis 530 |
| C67S | 1.1231 | 510 | 640 | 16 | 200 | 1140 | 315 | 1200 bis 1900 | 370 bis 580 |
| C75S | 1.1248 | 510 | 640 | 15 | 200 | 1170 | 320 | 1200 bis 1900 | 370 bis 580 |
| C85S | 1.1269 | 535 | 670 | 15 | 210 | 1190 | 325 | 1200 bis 2000 | 370 bis 600 |
| C90S | 1.1217 | 545 | 680 | 14 | 215 | 1200 | 325 | 1200 bis 2100 | 370 bis 600 |
| C100S | 1.1274 | 550 | 690 | 13 | 220 | 1200 | 325 | 1200 bis 2100 | 370 bis 630 |
| C125S | 1.1224 | 600 | 740 | 11 | 230 |
1200
| 325 | 1200 bis 2100 | 370 bis 630 |
| 48Si7 | 1.5021 | 580 | 720 | 13 | 225 | - | - | 1200 bis 1700 | 370 bis 520 |
| 56Si7 | 1.5026 | 600 | 740 | 12 | 230 | - | - | 1200 bis 1700 | 370 bis 520 |
| 51CrV4 | 1.8159 | 550 | 700 | 13 | 220 | - | - | 1200 bis 1800 | 370 bis 550 |
| 80CrV2 | 1.2235 | 580 | 720 | 12 | 225 | - | - | 1200 bis 1800 | 370 bis 550 |
| 75Ni8 | 1.5634 | 540 | 680 | 13 | 210 | - | - | 1200 bis 1800 | 370 bis 550 |
| 125Cr2 | 1.2002 | 590 | 750 | 11 | 235 | - | - | 1300 bis 2100 | 405 bis 630 |
| 102Cr6 | 1.2067 | 590 | 750 | 11 | 235 | - | - | 1300 bis 2100 | 405 bis 630 |
a Der Besteller darf Härtewerte oder Zugfestigkeitswerte verlangen, jedoch nicht beides. Falls nichts festgelegt wird, gelten die Zugfestigkeitswerte.
b Die Werte gelten für Dicken 0,30 mm ß t ß 3,00 mm. Bei dickerem Band müssen die Werte für die mechanischen Eigen_x005fschaften bei der Anfrage und Bestellung vereinbart werden.
c Für Erzeugnisse, die im kaltgewalzten Zustand geliefert werden, gelten Spannen von 150 N/mm2 oder 50 HV, z.B. 850 N/mm2 bis 1000 N/mm2 oder z. B. 240 HV bis 290 HV.
d Für Erzeugnisse, die im vergüteten Zustand geliefert werden, gelten Spannen von 150 N/mm2 oder 50 HV, z.B. 1350 N/mm2 bis 1500 N/mm2 oder z.B. 450 HV bis 500 HV.
e Rp0,2 0,2%-Dehngrenze; Rm Zugfestigkeit; A80 Bruchdehnung bei einer Anfangsmeßlänge von 80 mm; HV Vickershärte.
| Stahlbezeic hnung | Stahlbezeic hnung | Austenitisie rungs_x005 f_x005f_x0 05ftemper atur oC | Abkühlmed ium | Mindestwe rte der Härtea im gehärteten Zustand ohne Anlassen | Mindestwerte der Härtea im gehärteten Zustand ohne Anlassen |
| Kurzname | Werkstoff-number | Austenitisie rungs_x005 f_x005f_x0 05ftemper atur oC | Abkühlmed ium | HRCb | HVb |
| C55S | 1.1204 | 830 bis 860 | Öl | 55 | 600 |
| C60S | 1.1211 | 825 bis 855 | Öl | 57 | 640 |
| C67S | 1.1231 | 815 bis 845 | Öl | 59 | 670 |
| C75S | 1.1248 | 810 bis 840 | Öl | 60 | 700 |
| C85S | 1.1269 | 800 bis 830 | Öl | 61 | 720 |
| C90S | 1.1217 | 790 bis 820 | Öl | 61 | 720 |
| C100S | 1.1274 | 790 bis 820 | Öl | 61 | 720 |
| C125S | 1.1224 | 780 bis 810 | Öl | 62 | 750 |
| C48Si7 | 1.5021 | 840 bis 870 | Wasser | 52 | 540 |
| 56Si7 | 1.5026 | 840 bis 870 | Öl | 55 | 600 |
| 51CrV4 | 1.8159 | 840 bis 870 | Öl | 57 | 640 |
| 80CrV2 | 1.2235 | 840 bis 870 | Öl | 60 | 700 |
| 75Ni8 | 1.5634 | 820 bis 850 | Öl | 60 | 700 |
| 125Cr2 | 1.2002 | 820 bis 850 | Öl | 62 | 750 |
| 102Cr6 | 1.2067 | 820 bis 850 | Öl | 61 | 720 |
a Diese Mindestwerte gelten für einen Dickenbereich von 0,30 mm bis 3,00 mm.
b HRC Rockwellhärte (Härteskala C); HV Vickershärte.
Carbon steel and spring steel each have unique performance characteristics and play an important role in different fields. Carbon steel is widely used in many industries because of its strength, durability and machinability. Spring steel plays an important role in the field of spring manufacturing because of its high elasticity, wear resistance and fatigue resistance. Their wide range of applications offers a wealth of options and possibilities for industry.