410/430 Ferrite Stainless Steel Roll
Ferrite stainless steel has good corrosion resistance, thermal conductivity is better than austenite, thermal expansion coefficient is smaller than austenite, thermal fatigue resistance, adding the stabilizing element titanium, good mechanical properties of weld parts. Used for building decoration, fuel burner parts, household appliances, home appliance parts, etc.
|
Specification
|
Grade
|
Chemical Composition (wt%)
|
|
||||
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
||
|
ASTM
|
430
|
≤0.12
|
- |
≤1.00
|
≤0.040
|
≤0.030
|
16.00-18.00
|
|
JIS
|
SUS 430
|
≤0.12
|
- |
≤1.00
|
≤0.040
|
≤0.030
|
16.00-18.00
|
|
GB
|
10Cr17
|
≤0.12
|
- |
≤1.00
|
≤0.040
|
≤0.030
|
16.00-18.00
|
|
JIS
|
SUS 410L
|
≤0.03
|
≤1.00
|
≤1.00
|
≤0.040
|
≤0.030
|
11.00-13.50
|
| JIS | SUS 410S | ≤0.08 | ≤1.00 | ≤1.00 | ≤0.040 | ≤0.030 | 11.50-13.50 |
|
Specification
|
Grade
|
Mechanical Property
|
Physical Property
|
||||||
|
Yield (MPa)
|
Tensile (MPa)
|
Elongation %
|
HRB
|
Specific Heat
(J/g℃) |
Modulus of Elasticity
(KN/mm2) |
Coefficient of Heat Expanision
10-5cm/cm/℃ (20-100℃) |
Thermal Conductivity W/m℃
(100℃) |
||
| JIS | SUS 430 | ≥205 | ≥420 | ≥22 | ≤88 | 0.46 | 200 | 10.4 | 26.1 |
|
ASTM/GB
|
430/10Cr17
|
≥205
|
≥450
|
≥22
|
≤89
|
||||
|
JIS
|
SUS 410L
|
≥195
|
≥360
|
≥22
|
≤88
|
0.46
|
208 |
11.1
|
24.9
|
|
JIS
|
SUS 410S
|
≥205
|
≥410
|
≥20
|
≤88
|
0.46
|
200
|
10.8
|
24.9 |
|
Product
|
Thickness
(mm) |
Width
(mm) |
Length
(mm) |
Weight
(Ton) |
Surface Treatment | |
|
Coil
|
Hot Rolling
|
4.0~16.0
|
1000~1600
|
- |
30 max.
|
No.1 |
|
Cold Rolling
|
0.5~5.0
|
1000~1600
|
- | 2B | ||
|
Hardness
|
HV
|
TS(N/mm2)
|
YS(N/mm2)
|
EL(%)
|
Thickness
|
Product
|
|
1/4H
|
200-250
|
≥650
|
≥400
|
≥15
|
0.6-4.5
|
Skelp
Sheet Coil |
|
1/2H
|
250-310
|
≥780
|
≥675
|
≥6
|
0.6-4.5
|
|
|
3/4H
|
310-370
|
≥930
|
≥800
|
≥3
|
0.6-4.0
|
|
|
H
|
≥370
|
≥1130
|
≥950
|
- |
0.6-3.0
|
Coil |