23Q110
Grain-Oriented Electrical Steel
23Q110 grain-oriented electrical steel, high performance silicon steel material, used in power transformers and generators to improve energy efficiency and reduce magnetic loss.
| Type: | Oriented Silicon Steel | Technique: | Cold Rolled |
|---|---|---|---|
| Thickness: | 0.23 - 0.230001 Mm | Surface Treatment: | Coated |
| Shape: | Steel Coil | Standard: | AiSi, ASTM, Bs, DIN, GB, JIS |
| Tolerance: | ±3% | Processing Service: | Decoiling, Cutting |
| Grade: | 23Q110 | Application: | Transformer Core |
| Material: | Cold Rold Grain-Oriented Electrical Steel | Port: | Shanghai Port , China |
High Light: UI Laminations CRGO Steel, 23Q110 CRGO Steel, CRGO ui laminations
23Q110
Grain-Oriented Electrical Steel
Cold Rolled Silicon CRGO Steel UI Laminations 23Q110 Transformer Core
|
B(T)
|
50Hz
P(W/kg) |
S(VA/kg) |
60Hz
P(W/kg) |
S(VA/kg) |
B(T)
|
50Hz
P(W/kg) |
S(VA/kg) |
60Hz
P(W/kg) |
S(VA/kg) |
| 0.40 |
0.058
|
0.104
|
0.076
|
0.131
|
1.62 |
0.904
|
1.296
|
1.173
|
1.621
|
| 0.50 |
0.087
|
0.148
|
0.115
|
0.186
|
1.63 |
0.940
|
1.342
|
1.197
|
1.677
|
| 0.60 |
0.122
|
0.196 |
0.161
|
0.247
|
1.64 |
0.940
|
1.329 |
1.220
|
1.737
|
| 0.70 |
0.163
|
0.248
|
0.214
|
0.313
|
1.65
|
0.961
|
1.446
|
1.245
|
1.801
|
| 0.80 |
0.210
|
0.303
|
0.275
|
0.384
|
1.66 |
0.981
|
1.506
|
1.272
|
1.873
|
| 0.90 |
0.262
|
0.362
|
0.344
|
0.461
|
1.67 |
1.003
|
1.573
|
1.298
|
1.953
|
| 1.00 |
0.321
|
0.427
|
0.420
|
0.545
|
1.68 |
1.027
|
1.647
|
1.327 |
2.041
|
| 1.10 |
0.385
|
0.498 |
0.504
|
0.636
|
1.69 | 1.050 | 1.727 | 1.357 |
2.140
|
| 1.20 |
0.456
|
0.579
|
0.598
|
0.738 | 1.70 |
1.075
|
1.821
|
1.389
|
2.249
|
| 1.30 |
0.536
|
0.670
|
0.702
|
0.907 | 1.71 |
1.103
|
1.923
|
1.422
|
2.372
|
| 1.40 |
0.626
|
0.784
|
0.819 | 1.053 | 1.72 |
1.31
|
2.042
|
1.459
|
2.511
|
| 1.50 |
0.732
|
0.943 | 1.956 | 1.238 | 1.73 |
1.161
|
2.176
|
1.498
|
2.674
|
| 1.51 | 0.745 | 0.946 | 1.971 | 1.259 | 1.74 |
1.193
|
2.331
|
1.536
|
2.860
|
| 1.52 | 0.757 |
0.985
|
0.988
|
1.284 | 1.75 |
1.229
|
2.513
|
1.580
|
3.076
|
| 1.53 |
0.770
|
1.008
|
1.003
|
1.307 | 1.76 |
1.265
|
2.728
|
1.625
|
3.332
|
| 1.54 |
0.783
|
1.032
|
0.020
|
1.333 | 1.77 |
1.305
|
2.984
|
1.678
|
3.663
|
| 1.55 | 0.796 | 1.058 | 1.037 | 1.334 | 1.78 | 1.347 | 3.295 | 1.731 | 3.994 |
| 1.56 | 0.810 | 1.086 | 1.054 | 1.367 | 1.79 | 1.391 | 3.667 | 1.779 | 4.43 |
| 1.57 | 0.824 | 1.114 | 1.073 | 1.403 | 1.80 | 1.435 | 4.121 | 1.841 | 4.993 |
| 1.58 | 0.839 | 1.146 | 1.092 | 1.439 | 1.85 | 1.693 | 8.454 | 2.170 | 10.136 |
| 1.59 | 0.854 | 1.179 | 1.111 | 1.479 | 1.90 | 1.970 | 19.951 | 2.498 | 23.853 |
| 1.60 | 0.870 | 1.215 | 1.131 | 1.524 | 1.91 | 2.043 | 25.909 | 2.587 | 31.007 |
| 1.61 | 0.887 | 1.254 | 1.152 | 1.571 | 1.92 | 2.074 | 28.462 | 2.625 | 34.073 |
Core Loss
23Q110 (0.23 m m)
Test method : Epstein Test Apparatus
Specimen : 30mm wide X 300mm long were sheared in the rolling direction and subjected to SRA at 800℃ for 2tirs
Density : 7.65kg/dm
Core Loss
23Q110 (0.23 m m)
Test method : Epstein Test Apparatus
Specimen : 30mm wide X 300mm long were sheared in the rolling direction and subjected to SRA at 800℃ for 2tirs
Density : 7.65kg/dm
Core Loss
23Q110 (0.23 m m)
Test method : Epstein Test Apparatus
Specimen :30mm wide X 300mm long were sheared in the rolling direction and subjected to SRA at 800℃ for 2tirs
Density : 7.65kg/dm