Type:	Oriented Silicon Steel	Technique:	Cold Rolled
Thickness:	0.27 - 0.270001 Mm	Surface Treatment:	Coated
Shape:	Steel Coil	Standard:	AiSi, ASTM, Bs, DIN, GB, JIS
Tolerance:	±3%	Processing Service:	Decoiling, Cutting
Grade:	23Q110	Application:	Transformer Core
Material:	Cold Rold Grain-Oriented Electrical Steel	Port:	Shanghai Port , China

High Light: 27Q120 crgo core transformer, Silicon crgo core transformer, CRGO laminated core of transformer

B(T)	50Hz P(W/kg)	S(VA/kg)	60Hz P(W/kg)	S(VA/kg)	B(T)	50Hz P(W/kg)	S(VA/kg)	60Hz P(W/kg)	S(VA/kg)
0.40	0.072	0.106	0.094	0.134	1.62	0.963	1.252	1.261	1.591
0.50	0.107	0.152	0.140	0.193	1.63	0.979	1.289	1.283	1.636
0.60	0.148	0.203	0.193	0.257	1.64	0.997	1.329	1.305	1.684
0.70	0.192	0.256	0.239	0.317	1.65	1.014	1.372	1.327	1.736
0.80	0.244	0.316	0.305	0.393	1.66	1.033	1.421	1.350	1.793
0.90	0.300	0.379	0.381	0.477	1.67	1.051	1.473	1.373	1.856
1.00	0.364	0.449	0.466	0.568	1.68	1.072	1.534	1.398	1.927
1.10	0.463	0.526	0.561	0.669	1.69	1.094	1.602	1.424	2.006
1.20	0.514	0.611	0.666	0.781	1.70	1.116	1.677	1.451	2.095
1.30	0.599	0.705	0.783	0.907	1.71	1.140	1.764	1.481	2.197
1.40	0.695	0.820	0.910	1.053	1.72	1.166	1.864	1.511	2.312
1.50	0.802	0.963	1.052	1.238	1.73	1.191	1.978	1.544	2.448
1.51	0.813	0.981	1.068	1.259	1.74	1.220	2.110	1.580	2.604
1.52	0.826	1.000	1.085	1.284	1.75	1.249	2.261	1.619	2.787
1.53	0.839	1.020	1.100	1.307	1.76	1.284	2.446	1.657	2.999
1.54	0.851	1.040	1.116	1.333	1.77	1.316	2.655	1.700	3.253
1.55	0.864	1.061	1.116	1.333	1.78	1.353	2.915	1.745	3.559
1.56	0.877	1.084	1.151	1.387	1.79	1.391	3.220	1.792	3.927
1.57	0.889	1.105	1.167	1.415	1.80	1.431	3.593	1.842	4.373
1.58	0.903	1.131	1.186	1.447	1.85	1.655	7.361	2.122	8.867
1.59	0.917	1.158	1.203	1.478	1.90	1.889	17.276	2.418	20.776
1.60	0.932	1.187	1.222	1.512	1.91	1.932	20.598	2.474	24.763
1.61	0.946	1.217	1.241	1.550	1.92	1.978	24.609	2.531	29.591

Core Loss

27Q120 (0.27 m m)

Test method : Epstein Test Apparatus 

Specimen : 30mm wide X 300mm long were sheared in the rolling direction and subjected to SRA at 800℃ for 2tirs

Density : 7.65kg/dm

Core Loss

27Q120 (0.27 m m)

Test method :  Epstein Test Apparatus 

Specimen : 30mm wide X 300mm long were sheared in the rolling direction and subjected to SRA at 800℃ for 2tirs

Density :  7.65kg/dm

Core Loss

27Q120 (0.27 m m)

Test method :  Epstein Test Apparatus 

Specimen : 30mm wide X 300mm long were sheared in the rolling direction and subjected to SRA at 800℃ for 2tirs

Density :  7.65kg/dm