Aluminium Alloy

Aluminum alloy is a material composed of aluminum and other metal elements
with light weight, high strength characteristics, widely used in industrial and manufacturing fields.

GB/T 3880

Wrought aluminium and aluminium alloy plates，sheets and strips for general engineering sheet.

Because aluminum has good plasticity, corrosion resistance and thermal conductivity, and its alloys have the advantages of high strength, wear resistance and corrosion resistance. It is widely used in the field of automobile manufacturing. At the same time, the lightweight characteristics of aluminum and its alloys can reduce the overall weight of the car, which has advantages in terms of improving fuel economy, reducing emissions and increasing driving handling.

Material: A 3004 / A 5005 / A 5754 / A 5182 / A 6016

Type: Coil; Sheet; Plate

Thickness: ≥0.2mm

Width: Customers’ Requirement

Temper: OH 111/H112/H12/H14/H16/H18/H19/T4/T6/H24 H34/H26 H36/H28 H38

Application: General industrial aluminum and aluminum alloy rolled sheet and strip

Grade	Supply Status	Thickness (mm)	Tensile Rm/ (MPa)	Tensile Rm/ (MPa)	Specified non-proportional Elongation Rp0.2/(MPa)	Elongation after fracture /% (A 50mm)	Elongation after fracture /% a (A)	Bending radius b (90°)	Bending radius b(180°)
3004	O H111	＞0.20~0.50	155~200	≥ 60	≥ 60	≥ 13	—	0t	0t
3004	O H111	＞0.50~1.50	155~200	≥ 60	≥ 60	≥ 14	—	0t	0t
3004	O H111	＞1.50~3.00	155~200	≥ 60	≥ 60	≥ 15	—	0t	0.5t
3004	O H111	＞3.00~6.00	155~200	≥ 60	≥ 60	≥ 16	—	1.0t	1.0t
3004	O H111	＞6.0~12.5	155~200	≥ 60	≥ 60	≥ 16	—	2.0t	—
3004	O H111	＞12.5~50.0	155~200	≥ 60	≥ 60	—	≥ 14	—	—
3004	H12	＞0.20~0.50	190~240	≥ 155	≥ 155	≥ 2	—	0t	1.5t
3004	H12	＞0.50~1.50	190~240	≥ 155	≥ 155	≥ 3	—	0.5t	1.5t
3004	H12	＞1.50~3.00	190~240	≥ 155	≥ 155	≥ 4	—	1.0t	2.0t
3004	H12	＞3.00~6.00	190~240	≥ 155	≥ 155	≥ 5	—	1.5t	—
3004	H22 H32	＞0.20~0.50	190~240	≥ 145	≥ 145	≥ 4	—	0t	1.0t
3004	H22 H32	＞0.50~1.50	190~240	≥ 145	≥ 145	≥ 5	—	0.5t	1.0t
3004	H22 H32	＞1.50~3.00	190~240	≥ 145	≥ 145	≥ 6	—	1.0t	1.5t
3004	H22 H32	＞3.00~6.00	190~240	≥ 145	≥ 145	≥ 7	—	1.5t	—
3004	H14	＞0.20~0.50	220~265	≥ 180	≥ 180	≥ 1	—	0.5t	2.5t
3004	H14	＞0.50~1.50	220~265	≥ 180	≥ 180	≥ 2	—	1.0t	2.5t
3004	H14	＞1.50~3.00	220~265	≥ 180	≥ 180	≥ 2	—	1.5t	2.5t
3004	H14	＞3.00~6.00	220~265	≥ 180	≥ 180	≥ 3	—	2.0t	—
3004	H24 H34	＞0.20~0.50	220~265	≥ 170	≥ 170	≥ 3	—	0.5t	2.0t
3004	H24 H34	＞0.50~1.50	220~265	≥ 170	≥ 170	≥ 4	—	1.0t	2.0t
3004	H24 H34	＞1.50~3.00	220~265	≥ 170	≥ 170	≥ 4	—	1.5t	2.0t

Grade	Supply Status	Sample Status	Thickness/mm	T.S. Rm/( MPa)	Non-proportional Elongation Rp0.2/( MPa)	Elongation after fracture /% a (A 50mm)	Elongation after fracture /% a (A)	Bending radius b (90°)	Bending radius b (180°)
5005 5005A	O H111	O H111	＞0.20~0.50	100~145	≥ 35	≥ 15	—	0t	0t
5005 5005A	O H111	O H111	＞0.50~1.50	100~145	≥ 35	≥ 19	—	0t	0t
5005 5005A	O H111	O H111	＞1.50~3.00	100~145	≥ 35	≥ 20	—	0t	0.5t
5005 5005A	O H111	O H111	＞3.00~6.00	100~145	≥ 35	≥ 22	—	1.0t	1.0t
5005 5005A	O H111	O H111	＞6.0~12.50	100~145	≥ 35	≥ 24	—	1.5t	—
5005 5005A	O H111	O H111	＞12.5~50.0	100~145	≥ 35	—	≥ 20	—	—
5005 5005A	H12	H12	＞0.20~0.50	125~165	≥ 95	≥ 2	—	0t	1.0t
5005 5005A	H12	H12	＞0.50~1.50	125~165	≥ 95	≥ 2	—	0.5t	1.0t
5005 5005A	H12	H12	＞1.50~3.00	125~165	≥ 95	≥ 4	—	1.0t	1.5t
5005 5005A	H12	H12	＞3.00~6.00	125~165	≥ 95	≥ 5	—	1.0t	—
5005 5005A	H22 H32	H22 H32	＞0.20~0.50	125~165	≥ 80	≥ 4	—	0t	1.0t
5005 5005A	H22 H32	H22 H32	＞0.50~1.50	125~165	≥ 80	≥ 5	—	0.5t	1.0t
5005 5005A	H22 H32	H22 H32	＞1.50~3.00	125~165	≥ 80	≥ 6	—	1.0t	1.5t
5005 5005A	H22 H32	H22 H32	＞3.00~6.00	125~165	≥ 80	≥ 8	—	1.0t	—
5005 5005A	H14	H14	＞0.20~0.50	145~185	≥ 120	≥ 2	—	0.5t	2.0t
5005 5005A	H14	H14	＞0.50~1.50	145~185	≥ 120	≥ 2	—	1.0t	2.0t
5005 5005A	H14	H14	＞1.50~3.00	145~185	≥ 120	≥ 3	—	1.0t	2.0t
5005 5005A	H14	H14	＞3.00~6.00	145~185	≥ 120	≥ 4	—	2.0t	—
5005 5005A	H24 H34	H24 H34	＞0.20~0.50	145~185	≥ 110	≥ 3	—	0.5t	1.5t
5005 5005A	H24 H34	H24 H34	＞0.50~1.50	145~185	≥ 110	≥ 4	—	1.0t	1.5t
5005 5005A	H24 H34	H24 H34	＞1.50~3.00	145~185	≥ 110	≥ 5	—	1.0t	2.0t
5005 5005A	H24 H34	H24 H34	＞3.00~6.00	145~185	≥ 110	≥ 6	—	2.0t	—
5005 5005A	H16	H16	＞0.20~0.50	165~205	≥ 145	≥ 1	—	1.0t	—
5005 5005A	H16	H16	＞0.50~1.50	165~205	≥ 145	≥ 2	—	1.5t	—
5005 5005A	H16	H16	＞1.50~3.00	165~205	≥ 145	≥ 3	—	2.0t	—
5005 5005A	H16	H16	＞3.00~4.00	165~205	≥ 145	≥ 3	—	2.5t	—
5005 5005A	H26 H36	H26 H36	＞0.20~0.50	165~205	≥ 135	≥ 2	—	1.0t	—
5005 5005A	H26 H36	H26 H36	＞0.50~1.50	165~205	≥ 135	≥ 3	—	1.5t	—
5005 5005A	H26 H36	H26 H36	＞1.50~3.00	165~205	≥ 135	≥ 4	—	2.0t	—
5005 5005A	H26 H36	H26 H36	＞3.00~4.00	165~205	≥ 135	≥ 4	—	2.5t	—
5005 5005A	H18	H18	＞0.20~0.50	≥ 185	≥ 165	≥ 1	—	1.5t	—
5005 5005A	H18	H18	＞0.50~1.50	≥ 185	≥ 165	≥ 2	—	2.5t	—
5005 5005A	H18	H18	＞1.50~3.00	≥ 185	≥ 165	≥ 2	—	3.0t	—
5005 5005A	H28 H38	H28 H38	＞0.20~0.50	≥ 185	≥ 160	≥ 1	—	1.5t	—
5005 5005A	H28 H38	H28 H38	＞0.50~1.50	≥ 185	≥ 160	≥ 2	—	2.5t	—
5005 5005A	H28 H38	H28 H38	＞1.50~3.00	≥ 185	≥ 160	≥ 3	—	3.0t	—

Grade	Suppply Status	Sample Status	Thickness/mm	T.S. Rm/( MPa)	Non-proportional Elongation Rp0.2/( MPa)	Elongation after fracture /% a (A 50mm)	Elongation after fracture /% a (A)	Bending radius b (90°)	Bending radius b (180°)
5754	O H111	O H111	＞0.20~0.50	190~240	≥ 80	≥ 12	—	0t	0.5t
5754	O H111	O H111	＞0.50~1.50	190~240	≥ 80	≥ 14	—	0.5t	0.5t
5754	O H111	O H111	＞1.50~3.00	190~240	≥ 80	≥ 16	—	1.0t	1.0t
5754	O H111	O H111	＞3.00~6.00	190~240	≥ 80	≥ 18	—	1.0t
5754	O H111	O H111	＞6.0~12.50	190~240	≥ 80	≥ 18	—	2.0t
5754	O H111	O H111	＞12.5~100	190~240	≥ 80	—	17	—
5754	H12	H12	＞0.20~0.50	220~270	≥ 170	≥ 4	—	—
5754	H12	H12	＞0.50~1.50	220~270	≥ 170	≥ 5	—	—
5754	H12	H12	＞1.50~3.00	220~270	≥ 170	≥ 6	—	—
5754	H12	H12	＞3.00~6.00	220~270	≥ 170	≥ 7	—	0.5t	1.5t
5754	H22 H32	H22 H32	＞0.20~0.50	220~270	≥ 130	≥ 7	—	1.0t	1.5t
5754	H22 H32	H22 H32	＞0.50~1.50	220~270	≥ 130	≥ 8	—	1.5t	2.0t
5754	H22 H32	H22 H32	＞1.50~3.00	220~270	≥ 130	≥ 10	—	1.5t	—
5754	H22 H32	H22 H32	＞3.00~6.00	220~270	≥ 130	≥ 11	—	—	—
5754	H14	H14	＞0.20~0.50	240~280	≥ 190	≥ 3	—	—	—
5754	H14	H14	＞0.50~1.50	240~280	≥ 190	≥ 3	—	—	—
5754	H14	H14	＞1.50~3.00	240~280	≥ 190	≥ 4	—	—	—
5754	H14	H14	＞3.00~6.00	240~280	≥ 190	≥ 4	—	1.0t	2.5t
5754	H24 H34	H24 H34	＞0.20~0.50	240~280	≥ 160	≥ 6	—	1.5t	2.5t
5754	H24 H34	H24 H34	＞0.50~1.50	240~280	≥ 160	≥ 6	—	2.0t	2.5t
5754	H24 H34	H24 H34	＞1.50~3.00	240~280	≥ 160	≥ 7	—	2.5t	—
5754	H24 H34	H24 H34	＞3.00~6.00	240~280	≥ 160	≥ 8	—	—	—
5754	H16	H16	＞0.20~0.50	265~305	≥ 220	≥ 2	—	—	—
5754	H16	H16	＞0.50~1.50	265~305	≥ 220	≥ 3	—	—	—
5754	H16	H16	＞1.50~3.00	265~305	≥ 220	≥ 3	—	—	—
5754	H16	H16	＞3.00~6.00	265~305	≥ 220	≥ 3	—	1.5t	—
5754	H26 H36	H26 H36	＞0.20~0.50	265~305	≥ 190	≥ 4	—	2.0t	—
5754	H26 H36	H26 H36	＞0.50~1.50	265~305	≥ 190	≥ 4	—	3.0t	—
5754	H26 H36	H26 H36	＞1.50~3.00	265~305	≥ 190	≥ 5	—	3.5t	—
5754	H26 H36	H26 H36	＞3.00~6.00	265~305	≥ 190	≥ 6	—	—	—
5754	H18	H18	＞0.20~0.50	≥ 290	≥ 250	≥ 1	—	—	—
5754	H18	H18	＞0.50~1.50	≥ 290	≥ 250	≥ 2	—	—	—
5754	H18	H18	＞1.50~3.00	≥ 290	≥ 250	≥ 2	—	—	—
5754	H28 H38	H28 H38	＞0.20~0.50	≥ 290	≥ 230	≥ 3	—	—	—
5754	H28 H38	H28 H38	＞0.50~1.50	≥ 290	≥ 230	≥ 3	—	—	—
5754	H28 H38	H28 H38	＞1.50~3.00	≥ 290	≥ 230	≥ 4	—	—	—
5754	H112	H112	6.00~12.50	≥ 190	≥ 100	≥ 12	—	—	—
5754	H112	H112	＞12.5~25.0	≥ 190	≥ 90	—	≥ 10	—	—
5754	H112	H112	＞25.0~40.0	≥ 190	≥ 80	—	≥ 12	—	—
5754	H112	H112	＞40.0~80.0	≥ 190	≥ 80	—	≥ 14	—	—
5754	F	—	＞4.5~150.0	—	—	—	—	—	—

Grade	Suppply Status	Sample Status	Thickness /mm	T.S. Rm/( MPa)	Non-proportional Elongation Rp0.2/( MPa)	Elongation after fracture /% a (A 50mm)	Bending radius b (90°)	Bending radius b (180°)
5182	0H111	0H111	＞0.2~0.50	255~315	≥ 110	≥ 11	—	1.0t
5182	0H111	0H111	＞0.50~1.50	255~315	≥ 110	≥ 12	—	1.0t
5182	0H111	0H111	＞1.50~3.00	255~315	≥ 110	≥ 13	—	1.0t
5182	H19	H19	＞0.20~1.50	≥ 380	≥ 320	≥ 1	—	—
6016	T4	T4	0.40~3.00	170~250	80~140	≥ 24	0.5t	0.5t
6016	T6	T6	0.40~3.00	260~300	180~260	≥ 10	—	—

A. When both columns A50mm and A have values, A50mm is suitable for the thickness not greater than 12.5mm, and A is suitable for the thickness greater than 12.5mm.

B. t in the bending radius indicates the thickness of the materials. For the materials with both 90° and 180° bending, if the demander does not specify 90° or 180° bending, the bending radius can be selected by the supplier.