Stainless Steel

Stainless steel is a corrosion-resistant, strong and versatile sheet metal widely used in construction, industry and manufacturing, known for its weather resistance and aesthetics.

410 430 stainless steel coil

410/430 Ferrite Stainless Steel Roll

Ferrite stainless steel has good corrosion resistance, thermal conductivity is better than austenite, thermal expansion coefficient is smaller than austenite, thermal fatigue resistance, adding the stabilizing element titanium, good mechanical properties of weld parts. Used for building decoration, fuel burner parts, household appliances, home appliance parts, etc.

Specification Grade Chemical Composition (wt%)
C Si Mn P S Cr
ASTM 430 ≤0.12 – ≤1.00 ≤0.040 ≤0.030 16.00-18.00
JIS SUS 430 ≤0.12 – ≤1.00 ≤0.040 ≤0.030 16.00-18.00
GB 10Cr17 ≤0.12 – ≤1.00 ≤0.040 ≤0.030 16.00-18.00
JIS SUS 410L ≤0.03 ≤1.00 ≤1.00 ≤0.040 ≤0.030 11.00-13.50
JIS SUS 410S ≤0.08 ≤1.00 ≤1.00 ≤0.040 ≤0.030 11.50-13.50
Specification Grade Mechanical Property Physical Property
Yield (MPa) Tensile (MPa) Elongation % HRB Specific Heat (J/g℃) Modulus of Elasticity (KN/mm2) Coefficient of Heat Expansion 10-5cm/cm/℃ (20-100℃) Thermal Conductivity W/m℃ (100℃)
JIS SUS 430 ≥205 ≥420 ≥22 ≤88 0.46 200 10.4 26.1
ASTM/GB 430/10Cr17 ≥205 ≥450 ≥22 ≤89
JIS SUS 410L ≥195 ≥360 ≥22 ≤88 0.46 208 11.1 24.9
JIS SUS 410S ≥205 ≥410 ≥20 ≤88 0.46 200 10.8 24.9
Product Thickness (mm) Width (mm) Length (mm) Weight (Ton) Surface Treatment
Coil Hot Rolling 4.0~16.0 1000~1600 – 30 max. No.1
Cold Rolling 0.5~5.0 1000~1600 – 2B
Hardness HV TS(N/mm2) YS(N/mm2) EL(%) Thickness Product
1/4H 200-250 ≥650 ≥400 ≥15 0.6-4.5 Skelp
Sheet
Coil
1/2H 250-310 ≥780 ≥675 ≥6 0.6-4.5
3/4H 310-370 ≥930 ≥800 ≥3 0.6-4.0
H ≥370 ≥1130 ≥950 – 0.6-3.0 Coil