Chemical Composition & Physical Properties
Grade
|
Suppply Status
|
Sample Status
|
Thickness/mm
|
T.S.
Rm/( MPa) |
Non-proportional Elongation
Rp0.2/( MPa) |
Elongation after fracture /%
a
(A 50mm) |
Elongation after fracture /%
a
(A) |
Bending radius
b
(90°) |
Bending radius
b
(180°) |
6016
|
T4 | T4 |
0.40~3.00
|
170~250
|
80~140
|
≥ 24
|
- |
0.5t
|
0.5t
|
6016
|
T6 | T6 |
0.40~3.00
|
260~300
|
180~260
|
≥10
|
- | - | - |
A. When both columns A50mm and A have values, A50mm is suitable for the thickness not greater than 12.5mm, and A is suitable for the thickness greater than 12.5mm.
B. t in the bending radius indicates the thickness of the materials. For the materials with both 90° and 180° bending, if the demander does not specify 90° or 180° bending, the bending radius can be selected by the supplier.
C. For 2014, 2024 and 2219 alloy O plates with a thickness > 12.5mm ~ 25.00mm, the tensile sample is machined from the core material and shall not have an aluminum coating.